BJB Polyurethane TC-894 FR REV 1
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Polyurethane |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X6Idb0_BJB-Polyurethane-TC-894-FR-REV-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TC-894 FR REV 1 incorporates a non-mercury based catalyst system that produces a tough 80 shore D material with a 2.5 minute work time. This system can be used to hand pour or machine cast electronic enclosures and all types of parts requiring flame retardant characteristics. Product Highlights:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| UL File Number |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- 1 | 1.18 | g/cm³ | |
| -- 2 | 1.33 | g/cm³ | |
| -- | 1.30 | g/cm³ | ASTM D792 |
| Shrinkage 3 | 0.15 | % | ASTM D2566 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time | 3.0 | min | |
| Work Time 4(25°C) | 2.5 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cure Time (25°C) | 5.0 - 7.0 | day |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 78 - 82 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1720 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 42.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 21 | % | ASTM D638 |
| Flexural Modulus | 1940 | MPa | ASTM D790 |
| Flexural Strength | 69.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 31 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 85.6 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 75.6 | °C | ASTM D648 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1 MHz) | 3.24 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.014 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 70, mixing ratio by capacity: 79 | ||
| Component B | Mixing ratio by weight: 100, mixing ratio by capacity: 100 | ||
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity | Brookfield | ||
| 25°C 5 | 325 | cP | Brookfield |
| 25°C 6 | 1450 | cP | Brookfield |
| 25°C | 740 | cP | Brookfield |
| Demold Time (25°C) | 60 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Note: Reported physical properties are based on test specimens cured at an elevated temperature, 180°F.In order to achieve maximum physical properties, a post cure with heat is required. BJB recommends 24 hours at ambient temperature, 77°F (25°C), followed by 16 hours at 150-180°F (66-82°C). Support of the part may be required to prevent part deformation during heat cure. |
| Note Message | |
|---|---|
| 1 . | Part A |
| 2 . | Part B |
| 3 . | 12"x 1/2"x 1/2" |
| 4 . | 100g mass |
| 5 . | Part A |
| 6 . | Part B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pyramid™ PEEK KD2000 Injection Molded Shape | Polymics, Ltd. | PEEK | Pyramid™ PEEK |
| INEOS LLDPE LL6608AF | INEOS Olefins & Polymers Europe | LLDPE | INEOS LLDPE |
| IROGRAN® A 92 E 4738 | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| POLYfill PPC B10075 | Polykemi AB | PP Copolymer | POLYfill |
| Sylvin 7011EE-85 Blue 8349 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |