ACCUCOMP™ CP0406L
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X5sh0R_ACCUCOMP-CP0406L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUCOMP™ CP0406L is a Polypropylene Copolymer (PP Copolymer) product. It is available in North America. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.2 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 66 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1000 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 23.0 | MPa | |
| Break | 17.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 6.0 | % | |
| Break | 400 | % | |
| Flexural Modulus | 1000 | MPa | ASTM D790 |
| Flexural Strength | 29.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 180 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 76.0 | °C | |
| 1.8 MPa, Unannealed | 48.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® HDB 502 Phillips Process | Marco Polo International, Inc. | HDPE | MARPOL® |
| RAMTOUGH PZ307G4 | Polyram Ram-On Industries | PC | RAMTOUGH |
| TAROLON 2500 G3 | Taro Plast S.p.A. | PC | TAROLON |
| TUFNYL® RGF 43 BLACK | SRF Ltd. | Nylon 66 | TUFNYL® |
| Sylvin 9788F1 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |