ULTEM™ AUT210 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X585s4_ULTEM-AUT210-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Transparent, Thermoplastic Polyimide (TPI). Glass transition Temperature (Tg) of 227degC. Haze onset temperature of 212degC (SABIC IP method). Very low outgassing and plateout, for automotive lighting applications where highly metallized, reflective surfaces are required. Resin is a Dual-use item and is subject to export control restrictions under both U.S. 15 CFR , 774 and Annex I of Reg. (EC) 428/2009 as ECN 1C008. Diversion contrary to law is prohibited. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 11 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (360°C/5.0 kg) | 16.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.0 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3590 | MPa | ASTM D638 |
| -- | 3320 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 105 | MPa | ASTM D638 |
| Yield | 103 | MPa | ISO 527-2/5 |
| Break 3 | 88.0 | MPa | ASTM D638 |
| Break | 88.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 8.0 | % | ASTM D638 |
| Yield | 7.0 | % | ISO 527-2/5 |
| Break 5 | 75 | % | ASTM D638 |
| Break | 54 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 3330 | MPa | ASTM D790 |
| -- 7 | 3140 | MPa | ISO 178 |
| Flexural Strength 8(Yield, 50.0 mm Span) | 170 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 16 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 38 | J/m | ASTM D256 |
| 23°C | 37 | J/m | ASTM D256 |
| -30°C 10 | 4.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 2400 | J/m | ASTM D4812 |
| -30°C 12 | No Break | ISO 180/1U | |
| 23°C 13 | No Break | ISO 180/1U | |
| Instrumented Dart Impact (23°C, Total Energy) | 33.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 215 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 201 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 211 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 14 | 196 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 222 | °C | ASTM D1525 15 |
| -- | 221 | °C | ISO 306/B50 |
| CLTE | |||
| Flow : -40 to 150°C | 5.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 150°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 150°C | 5.0E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 150°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Metallized Haze Onset | 212 | °C | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 360 to 382 | °C | |
| Middle Temperature | 371 to 393 | °C | |
| Front Temperature | 382 to 404 | °C | |
| Nozzle Temperature | 377 to 399 | °C | |
| Processing (Melt) Temp | 382 to 404 | °C | |
| Mold Temperature | 135 to 163 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 120*10*4 mm |
| 15 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BMNO P40 | Arkema | Nylon 11 | Rilsan® |
| RTP 1300 MG 50 SI 2 | RTP Company | PPS | RTP |
| POLYLAC® PA-758R | CHI MEI CORPORATION | ABS | POLYLAC® |
| Reny® NXG5945S | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Ateva® 1941 | Celanese EVA Performance Polymers | EVA | Ateva® |