TECHNYL® A 118L V50 BLACK 2428
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X4l1I7_TECHNYL-A-118L-V50-BLACK-2428.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL A 118L V50 is a polyamide 6.6 reinforced with 50% of glass fiber, with thermal stability, UV protection and modified viscosity that provides better superficial appearance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.57 | g/cm³ | ASTM D792 |
| Water Absorption (23°C, 24 hr) | 0.60 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 13000 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 220 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 1.8 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 16800 | MPa | ISO 178 |
| Flexural Stress (23°C) | 355 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 60 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength (23°C) | 14 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | > 240 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | > 240 | °C | ISO 75-2/Af |
| Peak Melting Temperature | 260 | °C | ASTM D3418 |
| CLTE - Flow (23 to 85°C) | 1.5E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Nozzle Temperature | 280 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ DC-818.G001-8000 | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| Prime Polypro™ E111G | Prime Polymer Co., Ltd. | PP Homopolymer | Prime Polypro™ |
| MOSTEN MT 812 | UNIPETROL RPA | PP Random Copolymer | MOSTEN |
| NatureFlex™ 19NE30 | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| Sylvin 9077-90 Grey 9611 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |