LNP™ THERMOCOMP™ RC008H compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X3xWxX_LNP-THERMOCOMP-RC008H-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* RC008H is a compound based on Nylon 66 resin containing 40% Carbon Fiber. Added features of this material include: Electrically Conductive, Healthcare. Also known as: LNP* THERMOCOMP* Compound RC-1008 Product reorder name: RC008H |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.33 | g/cm³ | ASTM D792 |
| -- | 1.34 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 to 0.40 | % | |
| Across Flow : 24 hr | 0.40 to 0.60 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.54 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.78 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 32000 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 288 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 1.8 | % | ASTM D638 |
| Flexural Modulus 4(100 mm Span) | 26100 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 100 mm Span) | 429 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 110 | J/m | ASTM D256 |
| 23°C 6 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1200 | J/m | ASTM D4812 |
| 23°C 7 | 71 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 15.8 | J | ASTM D3763 |
| -- | 4.66 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 64.0 mm Span 8 | 261 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 255 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 9 | 252 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 4.9E-6 | cm/cm/°C | |
| Transverse : -30 to 30°C | 7.2E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® AR3XBK8510 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Nypol® PA A3 G30 M2 NTLA014 NR394 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Formolon® 1071 | Formosa Plastics Corporation, U.S.A. | PVC Homopolymer | Formolon® |
| OmniTech™ ABS 24 HH | OMNI Plastics, LLC | ABS | OmniTech™ |
| MAXAMID™ EPDMRC036-HSL-BK09 | Pier One Polymers, Inc. | Nylon 6 | MAXAMID™ |