Romiloy® 3020/01-4 M10
| Category: | ASA+Nylon , Acrylonitrile Styrene Acrylate + PA |
| Manufacturer: | ROMIRA GmbH |
| Trademark: | Romiloy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X3a84y_Romiloy3020014M10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Romiloy®3020/01-4 M10 is an acrylonitrile-styrene-acrylate + nylon (ASA + nylon) material, and the filler is 10% mineral filler. This product is available in Europe,. Romiloy®The main features of 3020/01-4 M10 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.16 | -- | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 32 | -- | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 0.50 - 0.80 | -- | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 1.0 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 2950 | 1700 | MPa | ISO 527-2/1 |
| Tensile Stress (23°C) | 52.0 | 37.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 50°C) | > 30 | -- | % | ISO 527-2 |
| Flexural Modulus 1(23°C) | 2400 | 1500 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 76.0 | 57.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.0 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 7.5 | 8.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 105 | -- | °C | ISO 75-2/B |
| Vicat Softening Temperature | 123 | -- | °C | ISO 306/B50 |
| CLTE - Flow (23 to 55°C) | 1.1E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bapolene® LD200B | Bamberger Polymers, Inc. | LDPE | Bapolene® |
| Eltex® TUB131N2010 | INEOS Olefins & Polymers Europe | HDPE Copolymer | Eltex® |
| ICORENE® 4007 | ICO Polymers EMEA, A Division of A. Schulman | PP Impact Copolymer | ICORENE® |
| LNP™ COLORCOMP™ PX99848 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ COLORCOMP™ |
| Lucopren® SB 1551-40S | Lucobit AG | SBS | Lucopren® |