LG ABS SH610A
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X3H1R2_LG-ABS-SH610A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LG ABS SH610A is an acrylonitrile butadiene styrene (ABS) material,. This product is available in North America, Latin America, Europe or Asia Pacific. The processing method is extrusion or injection molding. The main features of LG ABS SH610A are:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 | g/cm³ | ASTM D792 |
| -- | 1040 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 5.0 | g/10 min | ASTM D1238 |
| Melt volume-flow rate (220°C/10.0 kg) | 1.50 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | ASTM D955 |
| Water Absorption (Saturation) | 0.19 | % | ISO 62 3 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 98 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ISO 527-2 4 |
| Tensile Strength | |||
| Yield | 41.4 | MPa | ASTM D638 |
| Yield | 41.0 | MPa | ISO 527-2 5 |
| Tensile Strain | |||
| Yield | 5.0 | % | ISO 527-2 6 |
| Fracture | 30 | % | ASTM D638 |
| Tensile Elongation at Break | 20 | % | ISO 527-2 7 |
| Flexural Modulus | 2060 | MPa | ASTM D790 |
| Flexural Strength | 65.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA 8 | ||
| -30°C | 28.6 | kJ/m² | ISO 179/1eA |
| 23°C | 48.8 | kJ/m² | ISO 179/1eA |
| Charpy impact strength | ISO 179/1eU 9 | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.18 mm | 490 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 400 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 92.2 | °C | ASTM D648 |
| Glass Transition Temperature 10 | 110 | °C | ISO 11357-2 11 |
| Vicat Softening Temperature | |||
| -- | 103 | °C | ASTM D1525 |
| 50°C/h, B (50N) | 94.8 | °C | ISO 306 12 |
| Linear expansion coefficient | ISO 11359-2 13 | ||
| Flow | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 14 |
| Volume Resistivity | > 1.0E+13 | ohms·m | IEC 60093 15 |
| Relative Permittivity (1 MHz) | 2.80 | IEC 60250 16 | |
| Dissipation Factor (1 MHz) | 9.5E-3 | IEC 60250 17 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | HB | UL 94 | |
| 3.18 mm | HB | UL 94 | |
| Burning Behav. at thickness h (3.20 mm, UL) | HB | ISO 1210 18 |
| Additional Information |
|---|
| Melt Flow Rate, ASTM D1238, 200°C/5kg: 0.5 g/10minMelt Flow Rate, ASTM D1238, 230°C/3.8kg: 1.5 g/10min |
| Note Message | |
|---|---|
| 1 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 2 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 3 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 4 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 5 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 6 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 7 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 8 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 9 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 10 . | 10 °C/min |
| 11 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 12 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 13 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 14 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 15 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 16 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 17 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 18 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMORUN® 3855B/N | Mitsubishi Chemical Performance Polymers, Inc. | TPE | THERMORUN® |
| Badadur® PBT8 GF30 | Bada AG | PBT | Badadur® |
| Cheng Yu N6G3 HI | Cheng Yu Plastic Company Limited | Nylon 6 | Cheng Yu |
| Sylvin 8200-85 Grey 9579 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NEOFLON™ M-300P | DAIKIN AMERICA, INC. | PCTFE | NEOFLON™ |