Fibremod™ GB402HP
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Fibremod™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X2vben_Fibremod-GB402HP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fibremod™ GB402HP is a 40 % long glass fibre reinforced polypropylene grade intended for injection moulding and extrusion. The long glass fibres, chemically coupled to the polypropylene matrix, are providing outstanding mechanical properties such as high strength, high stiffness and excellent impact behaviour. Due to its excellent combination of properties this material can substitute in many applications other engineering plastics or metal alloys. A significant value of this material is the fact that it does not change its mechanical properties at humid conditions or water contact. The product is available in standard black. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | Internal method | ||
| Vertical flow direction : 2.00mm | 0.60 | % | Internal method |
| Flow direction : 2.00mm | 0.10 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 132/10) | 123 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 9000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, Injection Molded) | 140 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, Injection Molded) | 2.0 | % | ISO 527-2/50 |
| Flexural Modulus 2(Injection Molded) | 8400 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C, injection molding | 40 | kJ/m² | ISO 179/1eA |
| -20°C, injection molding | 32 | kJ/m² | ISO 179/1eA |
| 23°C, injection molding | 28 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C, injection molding | 55 | kJ/m² | ISO 179/1eU |
| 23°C, injection molding | 57 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -20°C, injection molding | 34 | kJ/m² | ISO 180/1A |
| 23°C, injection molding | 31 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 166 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 162 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 165 | °C | ISO 306/A50 |
| -- | 145 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Feeding Temperature: 40 to 80°CBack pressure: As low as possibleScrew speed: Low to mediumFlow front speed: 100 - 200 mm/s |
| Note Message | |
|---|---|
| 1 . | 150x80x2 mm |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8313-70FUV Natural | Sylvin Technologies Incorporated | PVC, Rigid | Sylvin |
| TOTAL Polypropylene PPC 4663 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| DeWAL DW 300-1 | DeWAL Industries | PI, TP | DeWAL |
| Dyna-Purge® SF | Dyna-Purge, division of Shuman Plastics | Proprietary | Dyna-Purge® |
| HAIPLEN H30 G2 BA | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |