TECAFORM® HPV13 is a brown homopolymer acetal with an internal PTFE lubricant. Its low coefficient of friction, excellent PV values, toughness, wear resistance, and machinability make it an exceptional material for use in manyindustrial and military components with moving parts. Additionally, TECAFORM® HPV13 has superior chemical resistance and flexural fatigue properties, as well as low moistureabsorption associated with acetal materials.

TECAFORM® HPV 13's range of exceptional properties makes it an ideal engineering plastic for use in precision instruments and measuring devices, as well as in many critical components in the automotive, aviation, military, industrial, food processing machinery, business equipment, and specialty valve areas.

General Information
Additive	PTFE lubricant
Features	Good dimensional stability Low friction coefficient Low hygroscopicity Homopolymer Impact resistance, good Machinable Good creep resistance Good chemical resistance Good wear resistance Good toughness Compliance of Food Exposure Elastic Self-lubricating
Uses	Valve/valve components Non-specific food applications Industrial application Military application Application in Automobile Field Business equipment
Agency Ratings	FDA 21 CFR 177.2480
Appearance	Brown
Forms	Shapes

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.50	g/cm³	ASTM D792
Water Absorption (23°C, 24 hr)	0.11	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale, 23°C)	118		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	2340	MPa	ASTM D638
Tensile Strength (Break, 23°C)	48.3	MPa	ASTM D638
Tensile Elongation (Break, 23°C)	10	%	ASTM D638
Flexural Modulus (23°C)	2410	MPa	ASTM D790
Flexural Strength (23°C)	86.2	MPa	ASTM D790
Coefficient of Friction
With self-dynamics ¹	0.12
With Self-Static	0.070
Wear Factor ²(0.28 MPa, 0.25 m/sec)	40	10^-8 mm³/N·m	ASTM D3702

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C)	53	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, not annealed	168	°C	ASTM D648
1.8 MPa, not annealed	118	°C	ASTM D648
Melting Temperature	175	°C
CLTE - Flow	9.2E-5	cm/cm/°C	ASTM D696
Maximum operating temperature- Long Term	85	°C

Additional Information	Nominal Value	Unit
Limiting Pressure Velocity - 10 fpm	12000	ft·lb/min
Data obtained from extruded shapes material.

Note Message
1 .	40 psi, 50 fpm
2 .	Against Steel

Resin Grade	Manufacturer	Category	Trademark
SABIC® PPcompound 90910CSU05	Saudi Basic Industries Corporation (SABIC)	PP, Unspecified	SABIC® PPcompound
Styrolution PS 1600	INEOS Styrolution Group GmbH	PS (GPPS)	Styrolution PS
TRIMID® N6-G13L	Polymer Technology and Services, LLC	Nylon 6	TRIMID®
Valtra® MA5210	Saudi Polymers Company	PS (HIPS)	Valtra®
Plexiglas® V044	Altuglas International of Arkema Inc.	Acrylic (PMMA)	Plexiglas®