LNP™ STAT-KON™ DX03571 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X0bGgr_LNP-STAT-KON-DX03571-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON DX03571 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound PDX-D-03571 Product reorder name: DX03571 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2900 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Break | 60.7 | MPa | |
| Break 2 | 60.7 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Break | 4.0 | % | |
| Break 3 | 4.0 | % | |
| Flexural Modulus | ASTM D790 | ||
| -- | 2830 | MPa | |
| 50.0 mm Span 4 | 2830 | MPa | |
| Flexural Strength | ASTM D790 | ||
| -- | 96.5 | MPa | |
| Break, 50.0 mm Span 5 | 96.5 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1100 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 121 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+4 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+2 to 1.0E+4 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALTECH® PA6 A 2045/500 GF45 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| CP PRYME® Polypropylene PPC100RC-35M | Chase Plastics Services Inc. | PP Random Copolymer | CP PRYME® Polypropylene |
| ENVIROPLAS® ENV08-NC870 | ENVIROPLAS®, Inc. | PBT | ENVIROPLAS® |
| SQUARE® LIM1550-40A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |
| Sylvin 9077-90 Grey 9611 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |