PULSE™ GX70 NAB
| Category: | PC+ABS , PC/ABS Engineering Resin |
| Manufacturer: | Trinseo |
| Trademark: | PULSE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Wz1pGn_PULSE-GX70-NAB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PULSE GX70 NAB is a PC/ABS blend, which provides an optimized balance of outstanding low temperature ductility, with low gloss, high heat resistance and easy flow. This resin provides low odor and VOC values, which make it especially suited for automotive interior applications. High flow and inherent low gloss, combined with excellent scratch resistance, produce exceptional part appearance and durability for molded in color applications. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ISO 1183/B |
| Apparent Density | 0.65 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/3.8 kg | 3.0 | g/10 min | |
| 260°C/5.0 kg | 17 | g/10 min | |
| Molding Shrinkage | 0.40 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (4.00 mm, Injection Molded) | 2300 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 4.00 mm, Injection Molded | 50.0 | MPa | |
| Break, 4.00 mm, Injection Molded | 45.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 4.00 mm, Injection Molded | 4.0 | % | |
| Break, 4.00 mm, Injection Molded | 130 | % | |
| Flexural Modulus 1(4.00 mm, Injection Molded) | 2500 | MPa | ISO 178 |
| Flexural Stress 2(4.00 mm, Injection Molded) | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 45 | kJ/m² | |
| 23°C | 50 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 45 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 96.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 116 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow : -30 to 80°C | 7.6E-5 | cm/cm/°C | |
| Transverse : -30 to 80°C | 7.8E-5 | cm/cm/°C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (2.00 mm) | < 80 | mm/min | FMVSS 302 |
| Carbon Emission | 10.0 | µg/g | VDA 277 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4594 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| TEREZ PA 8500 GF 19 GL | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA |
| Tufpet PBT G1010 | Mitsubishi Rayon America Inc. | PBT | Tufpet |
| Borlink™ LE4244S | Borealis AG | PE, Unspecified | Borlink™ |
| Cheng Yu NGC3 | Cheng Yu Plastic Company Limited | Nylon 6 | Cheng Yu |