Ultramid® B3EG7
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WyyWlO_Ultramid-B3EG7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid B3EG7 is a 35% glass fiber reinforced injection molding PA6 grade. Applications Typical applications include industrial articles and electrical insulating parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.41 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 45.0 | -- | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 6.2 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 11000 | 7200 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 200 | 130 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.5 | 7.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 10000 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 13 | -- | kJ/m² | |
| 23°C | 17 | 33 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 90 | -- | kJ/m² | |
| 23°C | 110 | 110 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 215 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| CLTE | ||||
| Flow | 1.7E-5 | -- | cm/cm/°C | |
| Transverse | 6.5E-5 | -- | cm/cm/°C | |
| RTI Elec | UL 746 | |||
| 0.750 mm | 120 | -- | °C | |
| 1.50 mm | 120 | -- | °C | |
| 3.00 mm | 120 | -- | °C | |
| RTI Imp | UL 746 | |||
| 1.50 mm | 95.0 | -- | °C | |
| 3.00 mm | 95.0 | -- | °C | |
| RTI Str | UL 746 | |||
| 1.50 mm | 130 | -- | °C | |
| 3.00 mm | 130 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+10 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.90 | 6.20 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.021 | 0.19 | ||
| 1 MHz | 0.021 | 0.19 | ||
| Comparative Tracking Index | 575 | 575 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 83.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.12 | % | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Yuyao PPO GFN2-501 | Yuyao Tenglong Plastics Co., Ltd. | PPE+PS | Yuyao PPO |
| APEX® 74-8208-A | Teknor Apex Company | PVC, Flexible | APEX® |
| Daelim Po1y® LL-05SU | DAELIM INDUSTRIAL CO., LTD. | LLDPE | Daelim Po1y® |
| LUVOCOM® 80/TF/22/NT | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |
| LEXAN™ HFD1034 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |