ATTANE™ SL 4101G
| Category: | ULDPE , Ultra Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ATTANE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Wyw8HZ_ATTANE-SL-4101G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ATTANE™SL 4101G ultra-low density polyethylene resin is used for blown film processing. This application requires a combination of excellent optical properties, tear resistance, impact resistance and very good heat sealing. The product also has very good kneading resistance. ATTANE SL4101G ultra-low density polyethylene resin contains slip agent and opening agent. Application field:
Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 0.912 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 2(190°C/2.16 kg) | 1.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| With Metal-Dynamic | 0.15 | ASTM D1894 | |
| With self-dynamics | 0.12 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 40 µm | 130 | MPa | ISO 527-3 |
| TD : 40 µm | 154 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 40 µm | 6.50 | MPa | ISO 527-3 |
| TD : Yield, 40 µm | 6.20 | MPa | ISO 527-3 |
| MD : Break, 40 µm | 32.0 | MPa | ISO 527-3 |
| TD : Break, 40 µm | 30.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 40 µm | 680 | % | ISO 527-3 |
| TD : Break, 40 µm | 800 | % | ISO 527-3 |
| Dart Drop Impact (40 µm) | 2700 | g | ISO 7765-1/A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 40 µm | 600 | g | ASTM D1922 |
| TD : 40 µm | 800 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature 3 | 92.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 40.0 µm) | 45 | ASTM D2457 | |
| Haze (40.0 µm) | 8.0 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 240 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜挤出的制造条件： 模具间隙 1.6 至 2.5 mm 熔体温度：190 至 240°C 放大比：1.5 比 3.5 建议的厚度范围：10 至 80 µm |
| Note Message | |
|---|---|
| 1 . | Compression molded sample |
| 2 . | Compression molded sample |
| 3 . | Compression molded sample |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP501D | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| TES J-4/35 BK223 | Techmer Engineered Solutions | Nylon 612 | TES |
| Wondel® A AN0F | Nanjing Julong Engineering Plastics Co., LTD | Nylon 66 | Wondel® A |
| PENTAMID B GV15 MK25 H natur | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |
| Sylvin 9067F4 Red 6263 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |