Ipethene® 810
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Carmel Olefins Ltd. |
| Trademark: | Ipethene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Wwmink_Ipethene-810.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| IPETHENE ® 810 is a low density polyethylene injection molding grade, produced by high pressure autoclave technology. It is a high MFR grade with excellent flow properties allowing short cycle time and easy filling of long flow-paths. The molded article is characterized by low degree of build in stress, low warpage, good stiffness and flexibility. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 45 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 9.00 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 130 | % | ISO 527-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 87.0 | °C | ISO 306 |
| Melting Temperature 1 | 108 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 160 to 220 | °C | |
| Mold Temperature | 10.0 to 40.0 | °C |
| Note Message | |
|---|---|
| 1 . | By DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 206F | RTP Company | Nylon 12 | RTP |
| WONDERLOY® PC-365 | CHI MEI CORPORATION | PC+ABS | WONDERLOY® |
| Di-Pak™ R-4354 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| KOPHOS® KO1375 | Kolon Plastics, Inc. | PC | KOPHOS® |
| Integra™ PC-5022 R UV 0001 | PolySource, LLC | PC | Integra™ |