Plenco 07579 (Compression)
| Category: | Phenolic , Phenolic |
| Manufacturer: | Plastics Engineering Co. |
| Trademark: | Plenco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WwGY5E_Plenco-07579-Compression-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLENCO 07579 is a fast curing, woodflour filled, novolac phenolic molding compound, formulated for industrial applications that do not require a smooth finish. UL recognized under component file E40654. 07579 is available in black. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Apparent Density | 0.60 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.42 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.64 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9240 | MPa | ASTM D638 |
| Tensile Strength | 45.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.50 | % | ASTM D638 |
| Flexural Modulus | 8390 | MPa | ASTM D790 |
| Flexural Strength | 76.1 | MPa | ASTM D790 |
| Compressive Strength | 193 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 24.9 | J/m | ASTM D256 |
| Notched Izod Impact | 24 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 179 | °C | ASTM D648 |
| Continuous Use Temperature | 187 | °C | ASTM D794 |
| CLTE - Flow | 7.5E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 12 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 5.10 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.046 | ASTM D150 | |
| Arc Resistance | 115 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 175 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (5.10 mm) | V-1 | UL 94 | |
| Oxygen Index | 25 | % | ASTM D2863 |
| Additional Information |
|---|
| The value listed as Comparative Tracking Index, UL 746 was tested according to ASTM D3638.The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.Post Shrinkage, ASTM D6289, 72hr, 120°C: 0.27%Drop Ball Impact, PLENCO Method: 175 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 0.50 | hr | |
| Mold Temperature | 165 - 182 | °C | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm |
| Injection instructions |
|---|
| Mold Close Time: 3-8 sec |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PC/TP-GP1 | Polymer Resources Ltd. | PC+Polyester | PRL |
| TEKNIFLEX® MED 3014-0180 | Tekni-Films, a div of Tekni-Plex | Film, PP | TEKNIFLEX® MED |
| Fainplast PVC GS 64/BT | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Hifax CA 1132 A | LyondellBasell Industries | TPO (POE) | Hifax |
| Mablex 459 | Ravago Group | PC+ABS | Mablex |