Clearflex® FG B3
| Category: | VLDPE , Very Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Clearflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WtgIck_Clearflex-FG-B3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clearflex FG B3 is a linear low density polyethylene, with antioxidants, slip and antiblocking agents, suitable for blown film technology. The product is characterised by a very low density and a high molecular weight. Films made by Clearflex FG B3 are highly transparent, have a good sealing, even at low temperature, and mechanical properties. It represent the version with slip and antiblock of Clearflex FG B0. Main Application Clearflex FG B3 is recommended for coextrusion to produce lamination film and is used in blend or coextrusion because of its unique properties. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.911 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | 0.15 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Recommended / Available | 10 to 50µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : Blown Film | 90.0 | MPa | |
| 1% Secant, TD : Blown Film | 100 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, Blown Film | 7.00 | MPa | |
| TD : Yield, Blown Film | 7.00 | MPa | |
| MD : Break, Blown Film | 35.0 | MPa | |
| TD : Break, Blown Film | 32.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, Blown Film | 500 | % | |
| TD : Break, Blown Film | 700 | % | |
| Dart Drop Impact 1(Blown Film) | 250 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD | 70.0 | kN/m | |
| TD | 110.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 88.0 | °C | ISO 306/A |
| Melting Temperature | 120 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, Blown Film) | 66 | ASTM D2457 | |
| Haze (Blown Film) | 7.0 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1483 HEC | RTP Company | PESU | RTP |
| Sanren F200 (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| TITANLENE® LDF 260GG | Lotte Chemical Titan (M) Sdn. Bhd. | LDPE | TITANLENE® |
| Elvax® 220W | DuPont Packaging & Industrial Polymers | EVA | Elvax® |
| TECHNYL® AR 218 V50 BLACK | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |