AKROMID® A3 GF 20 1 natural (1261)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WtQVDt_AKROMID-A3-GF-20-1-natural-1261-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 GF 20 1 natural (1261) is a 20% glass fibre reinforced and heat stabilised polyamide 6.6 with medium stiffness and strength and light inherent color, UL listed. Applications are mainly components in mechanical engineering and in the automotive industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.28 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 95.0 | -- | cm | Internal method |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction | 1.3 | -- | % | ISO 294-4 |
| Flow direction | 0.30 | -- | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 6.7 - 7.2 | -- | % | ISO 62 |
| Humidity Absorption - 62% RH (70°C) | 2.3 - 2.5 | -- | % | ISO 1110 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Temperature index | IEC 216 | |||
| 50% Loss of Tensile Strength, 20000 hr | 130 - 150 | -- | °C | IEC 216 |
| 50% Loss of Tensile Strength, 5000 hr | 160 - 175 | -- | °C | IEC 216 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 20 | -- | % | ISO 1172 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 210 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 7200 | 4600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 160 | 100 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.5 | 8.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 7000 | 5000 | MPa | ISO 178 |
| Flexural Stress 2 | 235 | 165 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 8.0 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 9.0 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 48 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 60 | 86 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 260 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 250 | -- | °C | ISO 75-2/A |
| Melting Temperature 3 | 262 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | -- | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Solanyl® BP blend 30F | Rodenburg Biopolymers B.V. | Biodeg Polymers | Solanyl® BP blend |
| Sumitomo Phenolic FM 4017F | Sumitomo Bakelite North America, Inc. | Phenolic | Sumitomo Phenolic |
| Ultramid® A3WG3 BK00564 | BASF Corporation | Nylon 66 | Ultramid® |
| Karina BLUE PVC COMPOUND 802-06/795-CRM | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lotryl® 29MA03 | Arkema | EMA | Lotryl® |