NEXUS ABS ABS450FR
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Nexus Resin Group, LLC. |
| Trademark: | NEXUS ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Wskecr_NEXUS-ABS-ABS450FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Molding Grade ABS |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2210 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 37.9 | MPa | ASTM D638 |
| Flexural Modulus | 2280 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 65.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 190 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 76.7 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.57 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 to 87.8 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 166 to 182 | °C | |
| Middle Temperature | 177 to 204 | °C | |
| Front Temperature | 191 to 232 | °C | |
| Nozzle Temperature | 191 to 232 | °C | |
| Processing (Melt) Temp | 191 to 232 | °C | |
| Mold Temperature | 48.9 to 76.7 | °C | |
| Back Pressure | 0.172 to 0.689 | MPa | |
| Screw Speed | 25 to 75 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP6021 | HMC Polymers | PP Homopolymer | Moplen |
| ESENTTIA 03H83 | Polipropileno del Caribe S.A. | PP Homopolymer | ESENTTIA |
| Maxxam™ H4 GF30 H black | PolyOne Corporation | PP Homopolymer | Maxxam™ |
| SEQUEL® 1718 FP NAT | LyondellBasell Industries | TPO (POE) | SEQUEL® |
| 3M™ Dyneon™ PTFE Compound TF 7196 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |