MAJORIS DT422 - 8229
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Wsb212_MAJORIS-DT422---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DT422 - 8229 is a black colour, 40% mineral filled polypropylene compound intended for injection moulding. The product is available in black DT422 - 8229 but other colours can be provided on request. DT422 - 8229 is intended for components which require good long term heat resistance, it has a high heat distortion temperature, good rigidity, low shrinkage, noice and vibration absorption and good dimensional stability. APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 5.5 | g/10 min | ISO 1133 |
| 230°C/5.0 kg | 22 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.50 - 0.70 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 88.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 33.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 2.5 | % | ISO 527-2/50 |
| Fracture | 6.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 4800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 1.4 | kJ/m² | ISO 179/1eA |
| 23°C | 1.6 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 11 | kJ/m² | ISO 179/1eU |
| 23°C | 21 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 2.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 144 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 86.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 158 | °C | ISO 306/A |
| -- | 97.0 | °C | ISO 306/B |
| CLTE - Flow | 5.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 750 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 - 270 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C | |
| Injection Rate | Slow-Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUTECH™ HP0339T30L | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| apilon 52® ESC 64 | API SpA | TPU-Polyester | apilon 52® |
| Celcon® LW90 | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| Exact™ 4151 Cast | ExxonMobil Chemical | Plastomer | Exact™ |
| XYLEX™ X2500UV resin | SABIC Innovative Plastics Asia Pacific | PC+PET | XYLEX™ |