Order Products : sales@su-jiao.com
LG ABS SG175
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WrngXK_LG-ABS-SG175.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Super Surface Gloss Application Electric&Electronic Products |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 | g/cm³ | ASTM D792 |
| -- | 1050 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 33 | g/10 min | ASTM D1238 |
| Melt volume-flow rate (220°C/10.0 kg) | 33.3 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.70 | % | ASTM D955 |
| Water Absorption (Saturation) | 0.20 | % | ISO 62 3 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile modulus | 2500 | MPa | ISO 527-2 4 |
| Tensile Strength | |||
| Yield, 3.20 mm 5 | 49.0 | MPa | ASTM D638 |
| Yield | 45.0 | MPa | ISO 527-2 6 |
| Tensile Strain | |||
| Yield | 6.0 | % | ISO 527-2 7 |
| Break, 3.20 mm 8 | 30 | % | ASTM D638 |
| Nominal strain at break | 15 | % | ISO 527-2 9 |
| Flexural Modulus 10(3.20 mm) | 2600 | MPa | ASTM D790 |
| Flexural Strength 11(3.20 mm) | 78.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy notched impact strength | ISO 179/1eA 12 | ||
| -30°C | 6.40 | kJ/m² | |
| 23°C | 17.2 | kJ/m² | |
| Charpy impact strength | ISO 179/1eU 13 | ||
| -30°C | 48.4 | kJ/m² | |
| 23°C | No Break | ||
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.20 mm | 23 | J/m | |
| 23°C, 6.40 mm | 200 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 86.0 | °C | ASTM D648 |
| Glass Transition Temperature 14 | 110 | °C | ISO 11357-2 15 |
| Vicat Softening Temperature | |||
| -- | 95.0 | °C | ASTM D1525 16 |
| 50°C/h, B (50N) | 95.9 | °C | ISO 306 17 |
| CLTE | ISO 11359-2 18 | ||
| Flow | 8.3E-5 | cm/cm/°C | |
| Transverse | 7.1E-5 | cm/cm/°C | |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 19 |
| Volume Resistivity | |||
| -- | 1.0E+16 | ohms·cm | ASTM D257 |
| -- | > 1.0E+13 | ohms·m | IEC 60093 20 |
| Dielectric Strength | |||
| -- | 28 | kV/mm | ASTM D149 |
| -- | 45 | kV/mm | IEC 60243-1 21 |
| Arc Resistance | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| High Amp Arc Ignition (HAI) (1.50 mm) | PLC 2 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 1.50 mm | PLC 4 | ||
| 3.00 mm | PLC 3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| -- | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Burning Behav. at thickness h (3.20 mm, UL) | HB | ISO 1210 22 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 to 90.6 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 191 to 210 | °C | |
| Middle Temperature | 199 to 221 | °C | |
| Front Temperature | 210 to 229 | °C | |
| Nozzle Temperature | 210 to 229 | °C | |
| Processing (Melt) Temp | 221 to 241 | °C | |
| Mold Temperature | 60.0 to 90.6 | °C | |
| Injection Pressure | 68.6 to 97.9 | MPa | |
| Back Pressure | 0.00 to 3.93 | MPa | |
| Screw Speed | 40 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | 50 mm/min |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | 50 mm/min |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | 15 mm/min |
| 11 . | 15 mm/min |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 14 . | 10 °C/min |
| 15 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 16 . | Rate A (50°C/h), Loading 2 (50 N) |
| 17 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 18 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 19 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 20 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 21 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 22 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vinnolit® K 725 F | Vinnolit GmbH & Co. KG | PVC Alloy | Vinnolit® |
| WELLAMID Nylon 6600 CF 30 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| Fainplast PVC KL 90/4 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| KOCETAL® WR301LOBK | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| LUVOCOM® 1-7497 VP | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |