LNP™ STAT-KON™ DX12411C compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Wreh5c_LNP-STAT-KON-DX12411C-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON DX12411C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Clean Compounding System. Also known as: LNP* STAT-KON* Compound DX12411C Product reorder name: DX12411C |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.85 | % | |
| Across Flow : 24 hr | 1.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.15 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.22 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2630 | MPa | ASTM D638 |
| -- | 2570 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 55.0 | MPa | ASTM D638 |
| Yield | 54.0 | MPa | ISO 527-2/5 |
| Break 3 | 47.0 | MPa | ASTM D638 |
| Break | 47.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 4.7 | % | ASTM D638 |
| Yield | 4.6 | % | ISO 527-2/5 |
| Break 5 | 19 | % | ASTM D638 |
| Break | 12 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2690 | MPa | ASTM D790 |
| -- 7 | 2540 | MPa | ISO 178 |
| Flexural Stress | 88.8 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 300 | J/m | ASTM D256 |
| 23°C 8 | 19 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 34.7 | J | ASTM D3763 |
| -- | 33.2 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 139 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 138 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 92.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 108 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 7.1E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 7.2E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 to 1.0E+6 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+3 to 1.0E+6 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYFORT® PP 2173 | A. Schulman Inc. | PP, Unspecified | POLYFORT® |
| Pro-fax PD702 | LyondellBasell Industries | PP Homopolymer | Pro-fax |
| Regis® 6100 | Noble Polymers | Polyolefin, Unspecified | Regis® |
| DAI-EL™ G-501NK | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |
| Sylvin 7833-85 Blue 8462 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |