DOWLEX™ 2083G
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Wqsge6_DOWLEX-2083G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Linear Low Density Polyethylene Excellent tear strength, outstanding toughness Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.925 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Puncture Resistance | |||
| 20 µm | 21.7 | J/cm³ | |
| 51 µm | 22.4 | J/cm³ | |
| Film strength | ASTM D882 | ||
| MD : 20 µm | 88.5 | J/cm³ | ASTM D882 |
| MD : 51 µm | 130 | J/cm³ | ASTM D882 |
| TD : 20 µm | 142 | J/cm³ | ASTM D882 |
| TD : 51 µm | 138 | J/cm³ | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 20 µm | 11.7 | MPa | ASTM D882 |
| MD : Yield, 51 µm | 11.0 | MPa | ASTM D882 |
| TD : Yield, 20 µm | 10.4 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 10.4 | MPa | ASTM D882 |
| MD : Break, 20 µm | 50.2 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 48.7 | MPa | ASTM D882 |
| TD : Break, 20 µm | 40.5 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 40.4 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm | 420 | % | ASTM D882 |
| MD : Fracture, 51 µm | 670 | % | ASTM D882 |
| TD : Break, 20 µm | 800 | % | ASTM D882 |
| TD : Fracture, 51 µm | 790 | % | ASTM D882 |
| Dart Drop Impact | ASTM D1709A | ||
| 20 µm | 94 | g | ASTM D1709A |
| 51 µm | 180 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm | 160 | g | ASTM D1922 |
| MD : 51 µm | 650 | g | ASTM D1922 |
| TD : 20 µm | 580 | g | ASTM D1922 |
| TD : 51 µm | 960 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 108 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 124 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 45°, 20.3 µm | 93 | ASTM D2457 | |
| 45°, 50.8 µm | 91 | ASTM D2457 | |
| Haze | ASTM D1003 | ||
| 20.3 µm | 1.2 | % | ASTM D1003 |
| 50.8 µm | 3.7 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Fabrication Conditions For Cast Film: Screw Size: 2.0 in. (51 mm); 30:1 L/D Melt Temperature: 524°F (273°C) Screw Size: 2.5 in. (63.5 mm); 30:1 L/D Melt Temperature: 525°F (274°C) Chill Roll Temperature: 70°F (21°C) Screw Speed: 30 rpm Line Speed: 600 fpm (183 m/min) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC V130-61FR | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| TOTAL Polypropylene PPC 7612 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Eleme HIG20060 | Eleme Petrochemical Company Ltd | HDPE | Eleme |
| KumhoSunny PC 2503NH | Shanghai KumhoSunny Plastics Co., Ltd. | PC | KumhoSunny PC |
| EnviroPro 1020GF45 | West Michigan Compounding | PP Copolymer | EnviroPro |