Borealis PP BC650MO
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Wq5ehq_Borealis-PP-BC650MO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BC650MO is a very high impact polypropylene heterophasic copolymer intended for injection moulding. This product offers a good UV resistance, further enhanced by pigmentation. This grade features high impact strength, high thermal stability and very good processability. As all polypropylenes, this grade shows excellent stresscracking and chemical resistances. This grade is characterized by combination of good stiffness, good creep resistance and very high impact strength even at low temperatures. This grade is mildly nucleated to maximize the mechanical stiffness. The additive formulation provides a smooth demoulding. Nucleation, good flow properties and high stiffness create a high potential for cycle time reduction. CAS-No. 9010-79-1 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.0 to 2.0 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1200 | MPa | ISO 527-2/50 |
| Tensile Stress (Yield) | 23.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 5.5 | % | ISO 527-2/50 |
| Flexural Modulus | 1100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 7.5 | kJ/m² | |
| 23°C | 25 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1(0.45 MPa, Unannealed) | 80.0 | °C | ISO 75-2/B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 230 to 260 | °C | |
| Mold Temperature | 10.0 to 30.0 | °C | |
| Injection Rate | Fast | ||
| Holding Pressure | 20.0 to 50.0 | MPa |
| Note Message | |
|---|---|
| 1 . | Injection molded specimen |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Novalloy-S S1100 (Type G) | Daicel Polymer Ltd. | PC+ABS | Novalloy-S |
| Chemraz 584 | Greene, Tweed & Co. | Perfluoroelastomer | Chemraz |
| EUROPLEX® Film HC 0F045 | Evonik Industries AG | PVDF+PMMA | EUROPLEX® Film |
| Isocor™ 6105 | Shakespeare Monofilaments and Specialty Polymers | Nylon 610 | Isocor™ |
| ACRYREX® CM-205M | CHI MEI CORPORATION | Acrylic (PMMA) | ACRYREX® |