VECTRA® J540
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | VECTRA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WpzxRL_VECTRA-J540.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
40% Mineral filled, high heat resistance. Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant FDA compliant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.74 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.37 | % | ISO 294-4 |
| Flow direction | 0.070 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 105 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.3 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 10000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 240 | °C | ISO 75-2/A |
| Melting Temperature 1 | 350 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 - 170 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Hopper Temperature | 20.0 - 60.0 | °C | |
| Rear Temperature | 335 - 345 | °C | |
| Middle Temperature | 340 - 350 | °C | |
| Front Temperature | 345 - 355 | °C | |
| Nozzle Temperature | 350 - 360 | °C | |
| Processing (Melt) Temp | 345 - 360 | °C | |
| Mold Temperature | 80.0 - 140 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 - 150 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 365 to 375°CZone 4 Temperature: 350 to 360°CFeed Temperature: 80 to 120°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecomid® NAX0 GR60 NL | Eurotec Engineering Plastics | Nylon 66 | Tecomid® |
| TAROMID A 260 | Taro Plast S.p.A. | Nylon 66/6 | TAROMID A |
| ELASTOSIL® E 91 | Wacker Chemie AG | Silicone | ELASTOSIL® E |
| Karina WHITE PVC COMPOUND 801-10/ 95-A-ERYB (**) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PENTAMID B GK30 H natur | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |