LNP™ STAT-LOY™ A3000 compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WmUTMW_LNPSTATLOYA3000compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON A3000 is a compound based on Acrylonitrile Butadiene Styrene resin. Added features of this material include: Antistat. Also known as: LNP* STAT-LOY* Compound A Product reorder name: A3000 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1700 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 38.0 | MPa | ISO 527-2/50 |
| Fracture | 29.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 3.1 | % | ISO 527-2/50 |
| Fracture | 21 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1800 | MPa | ISO 178 |
| Flexural Stress | 55.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 25 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | > 100 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, unannealed, 64.0mm span | 90.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 76.0 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 - 1.0E+12 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 - 0.10 | % | |
| Rear Temperature | 182 - 193 | °C | |
| Middle Temperature | 193 - 204 | °C | |
| Front Temperature | 204 - 216 | °C | |
| Processing (Melt) Temp | 199 - 210 | °C | |
| Mold Temperature | 10.0 - 48.9 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RJM SF402-E | RJM International, Inc. | PPE | RJM |
| ALTECH® PP-H A 2020/100 GF20 | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| POLYfill PP CPQ10015 FF | Polykemi AB | PP, Unspecified | POLYfill |
| SHINSTRA WG65BS TKB | Shinil Chemical Industry Co., Ltd. | Nylon 66 | SHINSTRA |
| Cellasto® MH24-45 | BASF Polyurethanes GmbH | TPU, Unspecified | Cellasto® |