Shinko-Lac® ABS HF-1
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Mitsubishi Rayon America Inc. |
| Trademark: | Shinko-Lac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WlmG03_Shinko-Lac-ABS-HF-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Shinko-Lac ABS HF-1 is a high flow, high modulus grade of ABS that is suitable for large or thin products and is effective for the remedies of sink marks, weld lines and molding cycle savings. Other features of HF-1 include an excellent balance of rigidity, strength, processability and glossiness. Typical applications of HF-1 include audio products, copying machine trays and furniture. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 113 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2650 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 44.1 | MPa | ASTM D638 |
| Flexural Modulus (23°C, 6.35 mm) | 2750 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C, 6.35 mm) | 70.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 6.35 mm | 59 | J/m | ASTM D256 |
| 0°C, 6.35 mm | 88 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 90.0 | °C | ASTM D648 |
| CLTE - Flow | 8.5E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat | 1670 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.21 | W/m/K | ASTM C177 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 180 - 250 | °C | |
| Middle Temperature | 180 - 250 | °C | |
| Front Temperature | 180 - 250 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 58.8 - 108 | MPa |
| Injection instructions |
|---|
| Higher mold temperature provides a product with excellent surface finish and less residual stress. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULATEC® PEEK CF 30 MV 14 | A. Schulman Europe | PEEK | SCHULATEC® |
| NYCOA Polyamide ASN 27 300 SR UV | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| Colorite Rigid PVC 2600 NAT | Colorite Polymers | PVC, Rigid | Colorite Rigid PVC |
| Evoprene™ HP 3710 | AlphaGary | SBC | Evoprene™ HP |
| HiFill® PA6/6 GF14 IM HS L | Techmer Engineered Solutions | Nylon 66 | HiFill® |