LNP™ STAT-KON™ DEF13 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WiNd9a_LNP-STAT-KON-DEF13-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* Stat-kon* DEF13 is a compound based on Polycarbonate resin containing Glass Fiber, Glass Fiber, Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* Stat-Kon* Compound DCF-1004 Product reorder name: DEF13 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption (24 hr) | 0.070 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 17900 | MPa | ASTM D638 |
| -- | 12400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 61.5 | MPa | ASTM D638 |
| Yield | 44.0 | MPa | ISO 527-2/5 |
| Break | 119 | MPa | ASTM D638 |
| Break | 12.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break | 4.0 | % | ASTM D638 |
| Break | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- | 9450 | MPa | ASTM D790 |
| -- 3 | 18500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 211 | MPa | ISO 178 |
| Break, 50.0 mm Span 4 | 159 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 96 | J/m | ASTM D256 |
| 23°C 5 | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C, 6.40 mm) | 510 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 147 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 100 mm Span 6 | 148 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 3.20 mm | 144 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 7 | 144 | °C | ISO 75-2/Ae |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 80*10*4 |
| 6 . | 120*10*4 mm |
| 7 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP GP1008FE | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Nycast CP | Cast Nylons Ltd. | Nylon 6 | Nycast |
| EMOPLEN® A 2540 T1 | EMAS Plastik San.Tic.AS. | PP, Unspecified | EMOPLEN® |
| LNP™ STAT-KON™ MD000I compound | SABIC Innovative Plastics Europe | PP, Unspecified | LNP™ STAT-KON™ |
| LEXAN™ 505RU resin | SABIC Innovative Plastics | PC | LEXAN™ |