Starex BC-0130 X
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WiMv6G_Starex-BC-0130-X.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Highly stiff ABS material that is mainly used for battery case |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 2.6 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 to 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 113 | ASTM D785 | |
| R-Scale | 115 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2400 | MPa | ASTM D638 |
| -- | 2600 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 48.0 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2/50 |
| Break 3 | 37.0 | MPa | ASTM D638 |
| Break | 38.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 14 | % | ASTM D638 |
| Break | 10 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2200 | MPa | ASTM D790 |
| -- 6 | 2700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 71.0 | MPa | ASTM D790 |
| -- 8 | 86.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 16 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 120 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 98 | J/m | ASTM D256 |
| 23°C 10 | 13 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 96.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 92.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 86.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 80.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 99.0 | °C | ISO 306/B50 |
| -- | 102 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 2.0 to 4.0 | hr | |
| Desiccant Dryer | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | < 0.10 | % | |
| Rear Temperature | 190 to 200 | °C | |
| Middle Temperature | 210 | °C | |
| Front Temperature | 210 to 220 | °C | |
| Nozzle Temperature | 230 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 88.3 | MPa | |
| Back Pressure | 0.981 to 1.96 | MPa | |
| Screw Speed | 50 to 90 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AIE PC 1010F-T6 | Asia International Enterprise (Hong Kong) Limited | PC | AIE PC |
| Estane® 5703 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Estane® |
| Karina WHITE PVC COMPOUND 10/1-FC (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PHOENIX™ 7652 | Phon Tech Industrial Company | TPE | PHOENIX™ |
| Petrothene® NA963083 | LyondellBasell Industries | LDPE | Petrothene® |