LONGLITE® PET 9130-104
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | CCP Group |
| Trademark: | LONGLITE® PET |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WhIaah_LONGLITE-PET-9130-104.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PET 9130-104 is a 30% glass fiber reinforced injection molding grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.70 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (270°C/2.16 kg) | 25 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.50 to 1.0 | % | |
| Flow | 0.10 to 0.30 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 11500 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 135 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 1.8 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 10000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 195 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.5 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 240 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 225 | °C | ISO 75-2/A |
| Melting Temperature | 254 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 22 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 140 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 265 to 300 | °C | |
| Mold Temperature | 100 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8454-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TABOREN PC 69 T 20 | SILON s.ro | PP Copolymer | TABOREN |
| Wellamid® XT1668-BK1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Anjacom® 450-GF30 | Almaak International GmbH | PBT | Anjacom® |
| Sumiliteresin® PR-53416 | SBHPP | Phenolic | Sumiliteresin® |