DuraSurf™ 4001 DuraJet
| Category: | UHMWPE , Ultra High Molecular Weight Polyethylene |
| Manufacturer: | Crown Plastics |
| Trademark: | DuraSurf™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WgZ7D4_DuraSurf-4001-DuraJet.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| As an alternative to high priced, non-durable high carbon formulas, DuraSurf™ 4001 DuraJet provides a blacker, faster alternative to our standard black base, without surrendering it's durability. The extremely high grade carbon also eliminates "bleeding" into other colors in die cut bases. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | > 0.930 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | 0.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow | 8.1 | % | |
| Across Flow | -0.20 | % | |
| Average Molecular Weight | |||
| -- | 8100000 | g/mol | |
| -- | 5400000 | g/mol | ASTM D4020 |
| Crystallinity | 44 | % | DSC |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Resistance - Sand Slurry | 0.570 | ||
| Tensile Modulus | 680 | MPa | ASTM D638, ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow | 2.0E-4 | cm/cm/°C | ASTM D696 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® HHM TR-232 | Chevron Phillips Chemical Company LLC | LLDPE | Marlex® |
| RTP 2800 B-75A FR A | RTP Company | TPV | RTP |
| Sarlink® TPV 24825N-1 | Teknor Apex Company | TPV | Sarlink® TPV |
| 4MID® 9B22115 HFR1 | 4Plas | Nylon 6 | 4MID® |
| Karina CRYSTAL PVC COM. (SP32811) -E 72/206-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Flexible | Karina |