Bio-Flex® F 6510
| Category: | Biodeg Polymers , Biodegradable Polymers |
| Manufacturer: | FKuR Kunststoff GmbH |
| Trademark: | Bio-Flex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WgQsXl_Bio-Flex-F-6510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bio-Flex ® F 6510 (prev. Bio-Flex® 682CF) Biodegradable compound for cast film extrusion made primarily from renewable resources. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Apparent Density | 0.80 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.5 - 4.5 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 2.50 - 4.50 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2600 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 47.0 | MPa | ISO 527-2 |
| Fracture | 23.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 19 | % | ISO 527-2 |
| Flexural Modulus | 2650 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 64.0 | MPa | ISO 178 |
| Tensile Strain at Tensile Strength | 4.0 | % | ISO 527 |
| Flexural Strain at Break | No Break | % | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability (20.0 µm) | 1.1 | cm³/m²/bar/24 hr | ISO 15105-2 |
| Nitrogen Permeability (20.0 µm) | 150 | cm³/m²/bar/24 hr | DIN 53380-2 |
| Water Vapor Transmission Rate (20 µm) | 130 | g/m²/24 hr | ISO 15106-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 60.0 | °C | ISO 306/A |
| Melting Temperature (DSC) | 150 - 170 | °C | ISO 3146 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.20 | % | |
| Cylinder Zone 1 Temp. | 170 | °C | |
| Cylinder Zone 2 Temp. | 180 | °C | |
| Cylinder Zone 3 Temp. | 180 | °C | |
| Cylinder Zone 4 Temp. | 190 | °C | |
| Adapter Temperature | 190 | °C | |
| Melt Temperature | < 190 | °C | |
| Die Temperature | 175 - 190 | °C |
| Extrusion instructions |
|---|
| Water jacket (feed): 35°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Royalstat R69 | Spartech Plastics | HDPE | Royalstat |
| Alkathene® Ultra LDD201 | Qenos Pty Ltd | LLDPE | Alkathene® Ultra |
| Anjacom® 050/75S | Almaak International GmbH | PC+ABS | Anjacom® |
| OnForce™ LFT PP-40LGF/001 Natural | PolyOne Corporation | PP Homopolymer | OnForce™ LFT |
| Plaskon SMT-B-1N | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |