PRL ABS-GP-HH
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WfgGLW_PRL-ABS-GP-HH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL ABS-GP-HH is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 1.0 to 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.18 mm) | 2210 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 44.8 | MPa | |
| Break, 3.18 mm | 42.1 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, 3.18 mm | 4.5 | % | |
| Break, 3.18 mm | 25 | % | |
| Flexural Modulus (3.18 mm) | 2480 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 79.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| -40°C, 3.18 mm | 53 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 190 | J/m | ASTM D256 |
| -40°C | 6.3 | kJ/m² | ISO 180/1A |
| 23°C | 13 | kJ/m² | ISO 180/1A |
| Gardner Impact (3.18 mm) | 22.6 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 102 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 90.6 | °C | |
| Vicat Softening Temperature | 116 | °C | ASTM D1525 1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 93.3 | °C | |
| Drying Time | 2.0 to 5.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 193 to 210 | °C | |
| Middle Temperature | 216 to 238 | °C | |
| Front Temperature | 227 to 254 | °C | |
| Processing (Melt) Temp | 232 to 274 | °C | |
| Mold Temperature | 48.9 to 82.2 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXAMID™ 226F5RY01 | SAX Polymers | Nylon 66 | SAXAMID™ |
| SLOVAMID® 6 GF 50 LS | Plastcom | Nylon 6 | SLOVAMID® 6 |
| Alathon® H6012 | LyondellBasell Industries | HDPE, MMW | Alathon® |
| AMTOPP BA30 | Inteplast Group | PP, Unspecified | AMTOPP |
| Polyrocks 5003N4 | Polyrocks Chemical Co., Ltd | PP, Unspecified | Polyrocks |