SILVER® PE 1011.MH
| Category: | LDPE+HDPE , Low Density Polyethylene + HDPE |
| Manufacturer: | Guangdong Silver Age Sci & Tech. Co., Ltd |
| Trademark: | SILVER® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WfNFtD_SILVER-PE-1011-MH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SlLVER® Modified Polyolefin includes modified polyethylene and modified polypropylene. Modified polyethylene is mainly applied to cable jacket. Black polyethylene compound is composed of polyethylene resin,carbon black, antioxidantand so on. Black polyehylene compound is applied to communication cable,contoll cable,signal cable,power cable,opticalcable and submarine cable. It conforms to GB15065-94 Standard. Modified PP including flame resistant, glass fiber andmineral reinforced and weather—resistant, is widely applied in electronic & electrical appliances, household appliances, autoaccessories, lightings, mechanical components and sockets, and so on. In addition, we develop new products according to customer's specific requirements. Characteristics:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 0.928 to 0.948 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | < 1.0 | g/10 min | |
| Environmental Stress-Cracking Resistance (F0) | > 500 | hr |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength | |||
| -- 1 | > 13.0 | MPa | |
| -- | > 14.0 | MPa | |
| Tensile Elongation | |||
| Break 2 | > 500 | % | |
| Break 3 | > 600 | % |
| Aging | Nominal Value | Unit | |
|---|---|---|---|
| Change in Tensile Strength | -25 to 25 | % | |
| Change in Ultimate Elongation | -25 to 25 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C |
| Electrical | Nominal Value | Unit | |
|---|---|---|---|
| Volume Resistivity | > 1.0E+6 | ohms·cm | |
| Dielectric Strength | > 25 | kV/mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 180 to 185 | °C | |
| Cylinder Zone 3 Temp. | 185 to 190 | °C | |
| Cylinder Zone 5 Temp. | 190 to 195 | °C | |
| Die Temperature | 195 to 200 | °C | |
| Extruder Screw L/D Ratio | 22.0:1.0 to 26.0:1.0 |
| Note Message | |
|---|---|
| 1 . | after oven aging |
| 2 . | after oven aging |
| 3 . | 100 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POPELEN AE-353CT | Lotte Chemical Corporation | PP Impact Copolymer | POPELEN |
| TEREZ POM 8005 GF25 | TER HELL PLASTIC GMBH | Acetal (POM) Copolymer | TEREZ POM |
| ACRYPET® VR S40 | Mitsubishi Rayon Co., Ltd. | Acrylic (PMMA) | ACRYPET® |
| ALCUDIA® LDPE 2221F | REPSOL | LDPE | ALCUDIA® LDPE |
| TECHNYL® C 218 V15 BLACK | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |