VENYL VG307 - 8020
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WebdWI_VENYL-VG307---8020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL VG307 - 8020 is a 30% glass fibre reinforced copolyamide 66/6 intended for Injection moulding. APPLICATIONS VENYL VG307 - 8020 has been developed especially for very demanding applications in automotive industry and electrical parts. Products requiring excellent combination between thermal and mechanical properties. VENYL VG307 - 8020 is available in both black standard (VENYL VG307 - 8229) and natural (VENYL VG307) but other colours can be provided on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.50 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.4 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 185 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 8900 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 40 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 241 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 235 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 242 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Oxygen Index | 23 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 255 to 265 | °C | |
| Front Temperature | 250 to 260 | °C | |
| Nozzle Temperature | 260 to 265 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Pressure | 85.0 to 100 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 60.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 3206 | Covestro - Polycarbonates | PC | Makrolon® |
| Nypol® PA A3 T40 VRD0240 NR373 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| AcryliMax 301HP | S&E Specialty Polymers, LLC | ABS | AcryliMax |
| Baydur® 728 IBS (55 pcf) | Covestro - PUR | PUR-MDI | Baydur® |
| Karina IVORY PVC COMPOUND 880-35/1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |