Order Products : sales@su-jiao.com
Stat-Tech™ LC-20NCF/000 V3 Natural
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Stat-Tech™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WeRA1Y_Stat-Tech-LC-20NCF-000-V3-Natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber for low to high levels of conductivity depending upon application requirements. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.050 to 0.10 | % | |
| Across Flow | 0.70 to 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 15800 | MPa | ASTM D638 |
| Tensile Strength (Break) | 93.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 1.0 | % | ASTM D638 |
| Flexural Modulus | 12200 | MPa | ASTM D790 |
| Flexural Strength | 145 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 27 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.35 mm | 260 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm | 206 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+4 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+2 to 1.0E+4 | ohms·cm | ASTM D257 |
| Shielding Effectiveness - 20MHz to 18GHz, 1/8" thickness | 30-80 | dB | |
| Static Decay - (Mil-B-81705C), 12% RH, 500 kV to 50 kV | 0.002 | sec |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 299 to 316 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ RC66-BK09 | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |
| Kuraray Poval® PVA 217SB | Kuraray Co., Ltd. | PVOH | Kuraray Poval® |
| Jianqiao Recycled PPGF30 | Shanghai Jianqiao Plastic Co., Ltd. | PP, Unspecified | Jianqiao |
| LNP™ THERMOCOMP™ RZ006S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Sylvin 8378-85 Green 3195 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |