TRIBOCOMP® PA66 CF30 TS7
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | EPIC Polymers |
| Trademark: | TRIBOCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WcVZiK_TRIBOCOMP-PA66-CF30-TS7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIBOCOMP® PA66 CF30 TS7 is a Polyamide 66 (Nylon 66) product filled with 30% carbon fiber and 15% ptfe fiber. It is available in Europe. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.37 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.4 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| 23°C | 22000 | 17000 | MPa | |
| 90°C | 15000 | -- | MPa | |
| 120°C | 11000 | -- | MPa | |
| Tensile Stress | ISO 527-2 | |||
| Yield, 23°C | 225 | 170 | MPa | |
| Yield, 90°C | 130 | -- | MPa | |
| Yield, 120°C | 120 | -- | MPa | |
| Tensile Strain (Break, 23°C) | 2.0 | -- | % | ISO 527-2 |
| Flexural Modulus (23°C) | 20000 | -- | MPa | ISO 178 |
| Flexural Stress (23°C) | 340 | 250 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 | |||
| vs. Itself - Dynamic | 0.14 | -- | ||
| vs. Itself - Static | 0.12 | -- | ||
| Wear Factor | 9.0 | -- | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 35 | -- | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 255 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 253 | -- | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 2.1E-5 | -- | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.51 | -- | W/m/K | ISO 22007 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+2 | -- | ohms | ASTM D257 |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 270 to 300 | °C | |
| Cylinder Zone 2 Temp. | 275 to 295 | °C | |
| Cylinder Zone 3 Temp. | 280 to 295 | °C | |
| Cylinder Zone 4 Temp. | 290 to 310 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP VLF 82109 | RTP Company | PEI | RTP |
| Bergamid™ B700 G15 H VN | PolyOne Corporation | Nylon 6 | Bergamid™ |
| Kingfa FRHIPSV-0 | Kingfa | PS (HIPS) | Kingfa |
| Optix® CA-81 FDA | Plaskolite, Inc. | Acrylic (PMMA) | Optix® |
| LGG 1043 | LG Polymers India Pvt. Ltd. | PS (GPPS) | LGG |