TOTAL Polyethylene Lumicene® Supertough 22ST05
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WZig48_TOTAL-Polyethylene-Lumicene-Supertough-22ST05.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lumicene® Supertough 22ST05 is a polyethylene blown film grade that is especially designed to have an excellent processability on extrusion and conversion lines and to give a very high toughness - stability balance allowing new innovative multilayer film concepts. Thanks to this innovative design, Lumicene® Supertough 22ST05 brings a huge down-gauging potential in the film market. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Stress | |||
| MD : Yield, 40 µm, blown film | 9.80 | MPa | ISO 527-3 |
| TD : Yield, 40 µm, blown film | 10.1 | MPa | ISO 527-3 |
| MD : Broken, 40 µm, blown film | 65.0 | MPa | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 60.0 | MPa | ISO 527-3/1B |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 630 | % | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 690 | % | ISO 527-3 |
| Dart Drop Impact (40 µm, Blown Film) | > 1000 | g | ISO 7765-1 |
| Elmendorf Tear Strength 1 | ISO 6383-2 | ||
| MD : 40.0 µm | 75.0 | kN/m | ISO 6383-2 |
| TD : 40.0 µm | 150.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 106 | °C | ISO 306 |
| Melting Temperature | 113 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 40.0 µm, Blown Film) | 60 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 7.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 - 230 | °C |
| Extrusion instructions |
|---|
| BUR: 1.5:1 to 4.5:1Die gap: 1.2 to 2.8 mm |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STABAMID® 26 JE 1 | Solvay Polyamide & Intermediates | Nylon 66 | STABAMID® |
| THERMOLAST® K TF5WKF (Series: DW) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Flontech® FT-930-RST | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| HiFill FR® PA6 GF15 FR-N | Techmer Engineered Solutions | Nylon 6 | HiFill FR® |
| LEXAN™ LAT4000 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |