Hiprolon® 11 ECN Black H8L P40
| Category: | Nylon 1012 , Polyamide 1012 |
| Manufacturer: | Arkema |
| Trademark: | Hiprolon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WYlet1_Hiprolon-11-ECN-Black-H8L-P40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hiprolon ® 11 ECN Black H8L P40 is a polyamide produced from a renewable source. This black grade is plasticized and designed for extrusion, particularly for cables sheathing applications. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (235°C/2.16 kg) | 9.00 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 64 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 30.0 | MPa | |
| Break | 54.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 49 | % | |
| Break | > 200 | % | |
| Flexural Modulus | 425 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 181 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ISO Shortname | PA 1012-P, KHL, 22-004 | ISO 1874 | |
| Renewable Carbon Conent | > 40 | % | ASTM D6866 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Melt Temperature | 210 to 260 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VERSIFY™ 3000 | The Dow Chemical Company | POP | VERSIFY™ |
| TRANSMARE® 10HGF30-0.001 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| VAMPSON L 4010 | Vamp Tech | PPS | VAMPSON |
| KOPLA PA6 KNG1090 | KOPLA Co., Ltd. | Nylon 6 | KOPLA PA6 |
| OnForce™ LFT 5200-5001 FR Natural | PolyOne Corporation | Polyolefin, Unspecified | OnForce™ LFT |