4DUR® 9K10000
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | 4Plas |
| Trademark: | 4DUR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WYkLqa_4DUR-9K10000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4DUR 9K10000 is a Extrusion Unfilled PBT |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (270°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Vertical flow direction | 1.6 | % | |
| Flow direction | 1.6 | % | |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2500 | MPa | ISO 527-2/5 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 55.0 | MPa | ISO 527-2/5 |
| Fracture, 23°C | 55.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 30 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 7.0 | kJ/m² | ISO 180/1A |
| 23°C | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 60.0 | °C | ISO 75-2/A |
| Melting Temperature 2 | 225 | °C | ISO 11357 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 60.0 - 100 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 40.0 - 80.0 | MPa | |
| Screw Speed | 300 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 50 - 70 °CBack Pressure: Low |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Melt Temperature | 240 - 260 | °C | |
| Die Temperature | 60.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 24 Hrs |
| 2 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 3M™ Dyneon™ PTFE TF 9207Z | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE |
| Chiao Fu PA66 MD212G23 NAT | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |
| Eco-Solutions GP335-13 | MINIMA Technoloy Co. Ltd. | Biodeg Polymers | Eco-Solutions |
| Hostacom TKC 199N | LyondellBasell Industries | PP Copolymer | Hostacom |
| LUVOCOM® 1105/TF/20/BN | Lehmann & Voss & Co. | PEEK | LUVOCOM® |