KRYSTALFLEX™ PE419
| Category: | PUR-Eth,aliphat , Polyurethane (Polyether, Aliphatic) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | KRYSTALFLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WY2UKM_KRYSTALFLEX-PE419.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| KRYSTALFLEX PE419 is a high performance aliphatic polyether film intended for processing by lamination into a range of glass/plastics components. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 70 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ASTM D412 | ||
| 100% strain | 2.07 | MPa | ASTM D412 |
| 300% strain | 6.89 | MPa | ASTM D412 |
| Tensile Strength 2(Yield) | 28.3 | MPa | ASTM D412 |
| Tensile Elongation 3(Break) | 550 | % | ASTM D412 |
| Tear Strength | 35.0 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -56.1 | °C | DSC |
| Additional Information |
|---|
| Softening Range, TMA: 120 to 255°FTypical Laminating Parameters:Ultimate Temperature: 194 to 230°FUltimate Pressure: 116 to 174 psiSoaking Time: 30 min/0.25 in |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Topilene® J440 | Hyosung Corporation | PP Impact Copolymer | Topilene® |
| Bergamid™ A700 G15 U-S0 BK035 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Ferro PP LPP20BA11WH | Ferro Corporation | PP Copolymer | Ferro PP |
| Keltan® 9950 | LANXESS Buna GmbH | EPDM | Keltan® |
| Dryflex® SE 50A301 | ELASTO | TPE | Dryflex® |