Bayfit® 566 (90 Index, 3.3 pcf)
| Category: | PUR-Ether/MDI , Polyurethane (Polyether, MDI) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Bayfit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WXvpLM_Bayfit-566-90-Index-3-3-pcf-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Bayfit 566 is a water-blown (MDI)/polyether based foam system used to manufacture high resilience (HR) cold-cure flex molded foam with medium to high load bearing properties. This system is characterized by good flow behavior in a wide variety of parts. Applications include office furniture, recreational seating, armrests and cushions. Bayfit 566 foam made at indices ranging from 80 to 105 typically passes the requirements of CAL-117 for flame resistance. Foams made at higher indices typically do not. As with any product, use of the Bayfit 566 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.0529 | g/cm³ | ASTM D3574 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 0.110 | MPa | ASTM D3574 |
| Tensile Elongation (Break) | 110 | % | ASTM D3574 |
| Tear Resistance | 446.4 | g/2.5 cm | ASTM D3574 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compression Set | ASTM D3574 | ||
| 50% | 3.3 | % | ASTM D3574 |
| 70% | % | ASTM D3574 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| IFD | ASTM D3574 | ||
| 25% R : 102 mm | 43.0 | lb/50 in² | ASTM D3574 |
| 65% R : 102 mm | 109 | lb/50 in² | ASTM D3574 |
| SAG Factor - 65%/25% IFD | 2.50 | ASTM D3574 | |
| Part A Appearance: Dark brown liquid Specific Gravity @ 25°C: 1.24 Viscosity: 28 cps Part B Appearance: Slightly hazy liquid Specific Gravity @ 25°C: 1.02 Viscosity: 1100 cps Cream Time: 10 secGel Time: 50 secFree Rise Density: 2.5 lb/ft³Component Temperature: 75 to 90°FMold Temperature: 100 to 130°FDemold Time: 3.5 to 5 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP HM3103A | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| TAROMID B 280 Z3 | Taro Plast S.p.A. | Nylon 6 | TAROMID B |
| TUFNYL® SGF 15 LEAFBROWN | SRF Ltd. | Nylon 6 | TUFNYL® |
| Globalene® 6733 | Lee Chang Yung Chemical Industry Corp. | PP Homopolymer | Globalene® |
| HONES® PPS HS-CT15-G | Guangdong Shunde Hones Polymer Material Co., Ltd. | PPS | HONES® |