Adiprene® L 275
| Category: | PUR-Ether/TDI , Polyurethane (Polyether, TDI) |
| Manufacturer: | Chemtura |
| Trademark: | Adiprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WWfBtZ_Adiprene-L-275.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
ADIPRENE L 275 is a polyether-based liquid urethane prepolymer which is readily processable by conventional hand and machine mixing techniques similar to those used for ADIPRENE L 315. ADIPRENE L 275 produces high quality vulcanizates in the 70-75 Shore D hardness range when cured with MBCA (4,4'-methylene-bis[o-chloroaniline]). These tough, high resilience elastomers have many unique features:
ADIPRENE L 275 has a longer working life when mixed with curatives than does ADIPRENE L 315, making it more suitable for the preparation of large parts. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.7 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 74 | ASTM D2240 | |
| Hardness - P & J | |||
| 21°C | 3.00 | ||
| 70°C | 4.00 | ||
| 100°C | 7.00 | ||
| 121°C | 8.50 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 758 | MPa | ASTM D790 |
| Compressive Strength | ASTM D695 | ||
| 10% Strain | 42.3 | MPa | |
| 25% Strain | 78.6 | MPa |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 35.0 | MPa | ASTM D412 |
| Tensile Strength | 49.1 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 230 | % | ASTM D412 |
| Tear Strength (Split) | 20 | kN/m | ASTM D470 |
| Compression Set 1(70°C, 22 hr) | 1.1 | % | ASTM D395A |
| Bayshore Resilience | 47 | % | ASTM D2632 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 960 to 1000 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 48.0 | °C | ASTM D648 |
| Brittleness Temperature | -54.0 | °C | ASTM D746 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 26 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Pot Life | 3.0 | min | |
| Post Cure Time (100°C) | 16 | hr |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Curing Time (100°C) | 1.0 | hr |
| Note Message | |
|---|---|
| 1 . | 2.8 MPa (400psi) load |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Colorite 11 Series 7011 | Colorite Polymers | PVC, Unspecified | Colorite 11 Series |
| Hanwha Total PE P110Y | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | HDPE | Hanwha Total PE |
| Hyflon® PFA P7010 | Solvay Specialty Polymers | PFA | Hyflon® PFA |
| OmniTech™ ABS 30 | OMNI Plastics, LLC | ABS | OmniTech™ |
| SABIC® BR 5510 | Saudi Basic Industries Corporation (SABIC) | PBR, High Cis | SABIC® BR |