Manner Flexible PVC X3582 TRN770
| Category: | PVC, Flexible , Flexible Polyvinyl Chloride |
| Manufacturer: | Manner Plastics, L.P. |
| Trademark: | Manner Flexible PVC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WWPAsO_Manner-Flexible-PVC-X3582-TRN770.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Recommended Applications: FDA (food grade) tubing and profile extrusion compound. This compound is recognized by NSF as complying with NSF/ANSI Standard 51. This product complies with the European Union Restriction on Hazardous Substances (RoHS) directive. |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 to 1.26 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A | 84 to 90 | ||
| Shore A, 15 sec | 77 to 83 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant 1 | 10.9 | MPa | ASTM D638 |
| Tensile Strength 2 | 20.9 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 390 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -27.0 | °C | ASTM D746 |
| Note Message | |
|---|---|
| 1 . | Unaged Dumbbells: .03 inch |
| 2 . | Unaged Dumbbells: .03 inch |
| 3 . | Unaged Dumbbells: .03 inch |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANAMID 6 B12^ F20 NH6 | Polykemi AB | Nylon 6 | SCANAMID 6 |
| Spartech Polycom PP5413 B1 | Spartech Polycom | PP, Unspecified | Spartech |
| DOW™ HDPE DMDA-8950 NT 7 | The Dow Chemical Company | HDPE | DOW™ HDPE |
| GELOY™ XP4025 resin | SABIC Innovative Plastics | ASA+PC | GELOY™ |
| Karina IVORY PVC COMPOUND 40904-35/2-L-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |