X-Pro SP 200 TF 30 3033
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | CTC Plastics, LLC |
| Trademark: | X-Pro |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WWBktg_X-Pro-SP-200-TF-30-3033.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CTC Plastics manufactures resins up to 99% recycled making them a lower cost alternative to virgin resins, while maintaining comparable quality and process ability. Clients can purchase resins directly to meet specifications or request CTC Plastics to create a custom resin from either of our two facilities. Our resins are customized per batch depending on compound needs. Different formulas can enhance strength, durability or flexibility. With our onsite certified lab, we are able to personalize the compound to your exact needs. Recycled resins lower cost, meet your exact specifications and reduce dependency on foreign oil by over 10 million gallons per year. Description: 30% Talc Reinforced Polypropylene, 98% recycled content Applications: Automotive , Industrial, Construction, Consumer, Lawn & Garden products, general purpose applications Color: General Purpose Black |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 - 17 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 14.5 | MPa | ASTM D638, ISO 527-2 |
| Flexural Modulus 1 | 1030 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 130 | J/m | ISO 180, ASTM D256 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 182 - 216 | °C | |
| Middle Temperature | 193 - 227 | °C | |
| Front Temperature | 204 - 216 | °C | |
| Nozzle Temperature | 204 - 216 | °C | |
| Processing (Melt) Temp | 204 - 216 | °C | |
| Mold Temperature | 26.7 - 60.0 | °C | |
| Injection Pressure | 3.45 - 10.3 | MPa | |
| Clamp Tonnage | 2.8 - 3.4 | kN/cm² |
| Injection instructions |
|---|
| Screw Speed: Medium to Fast |
| Note Message | |
|---|---|
| 1 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MBA ABS 4134 | MBA Polymers | ABS | MBA ABS |
| DENILUB PBT NEAT RESIN | Vamp Tech | PBT | DENILUB |
| ENFLEX VU-420-60A | Ravago Group | PP+EPDM | ENFLEX |
| KPOL-LDPE LD K-30/918 | KPOL Chem Co. | LDPE | KPOL-LDPE |
| Karina IVORY PVC COMPOUND 602D35/ 1-C-AT-IS (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |