Hanwha Total PE 520A
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WVVNo4_Hanwha-Total-PE-520A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 520A is a low-density polyethylene resin for extrusion coating applications. This grade is designed for cionventional t-die extrusion coating process. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.2 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 13.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 720 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 50 µm | 21.6 | MPa | ASTM D882 |
| TD : Break, 50 µm | 17.7 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm | 320 | % | ASTM D882 |
| TD : Break, 50 µm | 620 | % | ASTM D882 |
| Dart Drop Impact (50 µm) | 110 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 89.0 | °C | ASTM D1525 1 |
| Melting Temperature | 110 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (50.0 µm) | 10 | % | ASTM D1003 |
| Additional Information |
|---|
| Blocking, SAMSUNG TOTAL: 350 g/10cm³ |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 180 - 190 | °C | |
| Cylinder Zone 2 Temp. | 180 - 190 | °C | |
| Cylinder Zone 3 Temp. | 180 - 190 | °C | |
| Cylinder Zone 4 Temp. | 180 - 190 | °C | |
| Cylinder Zone 5 Temp. | 180 - 190 | °C | |
| Die Temperature | 170 - 180 | °C |
| Extrusion instructions |
|---|
| Blow up ratio: 1 to 2 |
| Note Message | |
|---|---|
| 1 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3687 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| WPP PP PPH6TF4C-Black | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| Globalene® 7633-3 | Lee Chang Yung Chemical Industry Corp. | PP Impact Copolymer | Globalene® |
| Grilon® BG-50 | EMS-GRIVORY | Nylon 6 | Grilon® |
| Karina MBU LILAC 34/151-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |