ULTEM™ CRS5011 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WUoseo_ULTEM-CRS5011-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Transparent, Enhanced flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming, UL94 V0 listing. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 11 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.70 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2900 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 100 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 60 | % | ASTM D638 |
| Flexural Modulus 4(100 mm Span) | 3100 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 100 mm Span) | 138 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Reverse Notch Izod Impact (3.20 mm) | 2100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 204 | °C | ASTM D648 |
| RTI Elec | 160 | °C | UL 746 |
| RTI Imp | 155 | °C | UL 746 |
| RTI Str | 160 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (3.20 mm, in Oil) | 18 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 3.20 | ||
| 60 Hz | 3.20 | ||
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 2.1E-3 | ||
| 60 Hz | 2.1E-3 | ||
| Arc Resistance 6 | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 4 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.47 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 343 to 366 | °C | |
| Middle Temperature | 354 to 377 | °C | |
| Front Temperature | 366 to 388 | °C | |
| Nozzle Temperature | 360 to 382 | °C | |
| Processing (Melt) Temp | 366 to 388 | °C | |
| Mold Temperature | 135 to 163 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VESTOSINT® 2155 natural color | Evonik Industries AG | Nylon 12 | VESTOSINT® |
| ACCUTECH™ CP0437G10CL | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| ISORENE™ A8-1001 | SABIC Innovative Plastics Europe | TPE | ISORENE™ |
| PermaStat® 1500-35D | RTP Company | TPE | PermaStat® |
| Vipel® K010-TBD-30 | AOC, L.L.C. | Vinyl Ester | Vipel® |