Vipel® F707-PVA-25
| Category: | Polyester Alloy , Polyester Alloy |
| Manufacturer: | AOC, L.L.C. |
| Trademark: | Vipel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WTEwVa_Vipel-F707-PVA-25.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vipel Corrosion Resistant Flexibilized, Isophthalic, NPG, Polyester Resin DESCRIPTION AOC's Vipel F707-PVA series are isophthalic-NPG, two stage, unsaturated polyester resins. The wet-out, cure and handling characteristics are typical of general purpose resins. BENEFITS PVC Bonding - Laminates made with Vipel F707-PVA resin bond to PVC. Versatile Suitable for various fabricating methods such as hand lay-up, spray-up and filament winding. Food and Drug All resins listed on this product data sheet are manufactured from raw materials that are listed in FDA regulation Title 21 CFR 177.2420. It is the fabricators responsibility to also be sure that the final composite is well cured. All composites used for FDA applications should be post cured at 180°F/82°C for at least 4 hours. After post curing , laminate should be washed with soap and water and rinsed. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | |
| Styrene Content | 48 | % |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Exotherm | |||
| Gel to Peak | 20.0 | min | |
| Peak | 185 | °C | |
| Gel Time (25°C) 1 | 25.0 | min |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Thixotropic Index | 2.00 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3860 | MPa | ASTM D638 |
| Tensile Strength | 86.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.7 | % | ASTM D638 |
| Flexural Modulus | 4070 | MPa | ASTM D790 |
| Flexural Strength | 138 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 78.3 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Mix Viscosity 2(25°C) | 500 | cP | |
| Post Cure Time (82°C) | 4.0 | hr |
| Note Message | |
|---|---|
| 1 . | Gel Time with 1.0% MEKP |
| 2 . | LV viscosity spindle 3 at 60 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G10 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Sinvicomp SRP5610 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Skyrol® SP19H | SKC Inc. | PET | Skyrol® |
| Bayblend® T90 XF | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| POLYFLAM® RIPP 4000 E CS1 | A. Schulman Europe | PP Copolymer | POLYFLAM® |