Hostacom M4 N01 L201218
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WSqc9e_Hostacom-M4-N01-L201218.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| "Hostacom" M4 N01 L201218 is a 40% mineral filled PP homopolymer, detergent resistance. The product is designed for injection molding of washing machine parts and is available in Whirlpool "global white" / color code 90201. UL listing in white and grey. It is not intended for medical, pharmaceutical or drinking water applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 11 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/5.0 kg) | 11.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 90.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant | 3600 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 32.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 4.0 | % | |
| Break | > 4.0 | % | |
| Flexural Modulus - Secant | 3900 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 50.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 1.5 | kJ/m² | |
| 23°C | 2.8 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 15 | kJ/m² | |
| 23°C | 28 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 75.0 | °C | ISO 75-2/A |
| RTI Elec | UL 746 | ||
| 1.00 mm | 65.0 | °C | |
| 1.50 mm | 65.0 | °C | |
| 3.00 mm | 65.0 | °C | |
| RTI Imp | UL 746 | ||
| 1.00 mm | 65.0 | °C | |
| 1.50 mm | 65.0 | °C | |
| 3.00 mm | 65.0 | °C | |
| RTI Str | UL 746 | ||
| 1.00 mm | 65.0 | °C | |
| 1.50 mm | 65.0 | °C | |
| 3.00 mm | 65.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm, GY, WT | HB | ||
| 1.50 mm, GY, WT | HB | ||
| 3.00 mm, GY, WT | HB |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Color Number | 90201 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAMAT 5003S1 | POLYROCKS CHEMICAL CO., LTD | PP, Unspecified | SAMAT |
| Celstran® +PP-GF40-04CN15/10 | Celanese Corporation | PP, Unspecified | Celstran® |
| Flexil™ 20S | Polymer Dynamix | Nylon 66 | Flexil™ |
| Leona™ FR250 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| Sylvin 9604-80 Clear Black 2105 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |