NILENE® P K50VA S
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | NILENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WRbZh6_NILENE-P-K50VA-S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene homopolymer 50% glass fibers reinforced chemically coupled, heat stabilized, good mechanical properties, flame rating UL94HB. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.34 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.40 - 0.55 | % | Internal method |
| Flow direction | 0.20 - 0.35 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 110 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.7 | % | ISO 527-2/1 |
| Flexural Modulus 1 | 7700 | MPa | ISO 178 |
| Flexural Stress 2 | 138 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 75 | J/m | ASTM D256 |
| 23°C | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 150 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 156 | °C | ISO 306/A50 |
| -- | 144 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 3(2.00 mm) | < 100 | mm/min | ISO 3795 |
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | UL 94 | |
| 1.50 mm | HB | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 650 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | IEC 60695-2-13 |
| Oxygen Index | 21 | % | ASTM D2863 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content 4(600°C) | 50 | % | ISO 3451 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 220 - 250 | °C | |
| Mold Temperature | 50.0 - 70.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Pre-heat Temperature: 70 to 80°CPre-heat Time: 1 hr |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 1.0 mm/min |
| 3 . | US FMVSS302 |
| 4 . | 1 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP520M | LyondellBasell Industries | PP Homopolymer | Moplen |
| Vydyne® R535 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| DuraElast 910-6 | Evermore Chemical Industry Co., Ltd. | TPU, Unspecified | DuraElast |
| Karina WHITE PVC COMPOUND -E500-10/1-BT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Pearlbond™ 508 | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlbond™ |