Trexprene® A70CI-HF
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Mitsubishi Chemical Performance Polymers, Inc. |
| Trademark: | Trexprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WRPQPZ_Trexprene-A70CI-HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Product Description: TREXPRENE ® A70CI-HF is a heat stabilized and UV Stabilized PP/EPDM based Thermoplastic Vulcanized Elastomer (TPV). This high flow, pre-colored compound is intended primarily for injection molding applications where longer flow distances and good surface appearance is needed. The material is primarily for interior applications. This material can be processed using Injection Molding, Extrusion, Blow Molding or other melt processing techniques. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 to 0.990 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 15 sec) | 70 to 78 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ISO 37 | ||
| Across Flow : 100% Strain | 2.80 | MPa | |
| Flow : 100% Strain | 3.60 | MPa | |
| Tensile Stress 2 | ISO 37 | ||
| Across Flow : Break | 5.50 | MPa | |
| Flow : Break | 5.70 | MPa | |
| Tensile Elongation 3 | ISO 37 | ||
| Across Flow : Break | 620 | % | |
| Flow : Break | 510 | % | |
| Tear Strength 4 | ISO 34-1 | ||
| Across Flow | 27 | kN/m | |
| Flow | 27 | kN/m | |
| Compression Set | |||
| 70°C, 24 hr | 33 | % | ASTM D395B |
| 70°C, 24 hr 5 | 33 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (110°C, 1000 hr) | -1.0 | % | ISO 188 |
| Change in Tensile Strain at Break in Air (110°C, 1000 hr) | -10 | % | ISO 188 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | |||
| -- | -53.0 | °C | ASTM D746 |
| Type B | -53.0 | °C | ISO 812 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 19 | mm/min | ISO 3795 |
| Fogging - Dry Fog | 86 | % | SAE J1756 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color Fastness | |||
| to Burnt Gas, AATCC Rating : 60°C 6 | > 4.00 | ||
| to Burnt Gas, Change in Color : 60°C 7 | Delta E < 3 | ||
| to Burnt Gas, Yellowness Index : 60°C 8 | < 2.00 | YI | |
| to Light 9 | Delta E < 3 | ||
| Odor Rating 10 | > 7.00 | ||
| Ozone Resistance (40°C) 11 | 0 Rating | ISO 1431-1 | |
| Weatherability | |||
| Arizona 12 | Delta E < 3 | ||
| Florida 13 | Delta E < 3 | SAE J1976 |
| Note Message | |
|---|---|
| 1 . | Type 1, 500 mm/min |
| 2 . | Type 1, 500 mm/min |
| 3 . | Type 1, 500 mm/min |
| 4 . | Method Ba, Angle (Unnicked), 500 mm/min |
| 5 . | Type A |
| 6 . | ISO 105-G02, AATCC TM 23, 168 h |
| 7 . | ISO 105-G02, AATCC TM 23, 168 h |
| 8 . | ISO 105-G02, AATCC TM 23, 168 h |
| 9 . | SAE J2412, ISO 105-B06, Cond. 5, 1,240.8 kJ/m² |
| 10 . | GMW3205 Code B |
| 11 . | 100 pphm, Method A |
| 12 . | 105,000 TNR Langleys exposure per GMW3417 L1, F2, G1, T5 |
| 13 . | 2 years exposure, Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SZF6208 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Fainplast PVC GS 69/P | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Durethan® C 38 FA 000000 | LANXESS Asia/Pacific | Nylon 6 | Durethan® |
| Generic XLPE | Generic | XLPE | Generic |
| Plaslube® ABS 7000 | Techmer Engineered Solutions | ABS | Plaslube® |